Glass ionomer cement, process of production and use thereof european Patent Office ep 3079645 B1

-
Lower limit: at least 1 or at least 3 or at least 5 wt.%;
-
Upper limit: utmost 50 or utmost 40 or utmost 30 wt.%;
-
Range: from 1 to 50 or from 3 to 40 or from 5 to 30 wt.%.
[0105] If the amount of the polyacid is too high, obtaining a workable consistency of the obtained paste when mixing
the compositions contained in the parts of the kit of parts described in the present text might become difficult. Further
mixing of the compositions might become difficult. In addition the obtained mixture or composition might become too
sticky (i.e. adheres to the dental instrument used for application).
[0106] If the amount of the polyacid is too low, obtaining a workable consistency of the obtained paste when mixing
the compositions contained in the parts of the kit of parts described in the present text might become difficult, either.
Further, it will become difficult to achieve the desired mechanical properties.
[0107] The cement composition described in the present text contains water. The water can be distilled, de-ionized,
or plain tap water. Typically, deionized water is used. The amount of water should be sufficient to provide adequate
handling and mixing properties and to permit the transport of ions, particularly in the filler-acid reaction.
[0108] The water is typically present in the following amounts (wt.% with respect to the weight of the whole composition
obtained when mixing the compositions contained in the kit of parts):
-
Lower limit: at least 5 or at least 7 or at least 9 wt.%;
-
Upper limit: utmost 16 or utmost 14 or utmost 12 wt.%;
-
Range: from 5 to 16 or from 7 to 14 or from 9 to 12 wt.%.
[0109] If the amount of the water is too low, obtaining a workable consistency of the obtained paste when mixing the
compositions contained in the parts of the kit of parts described in the present text might become difficult. Further mixing
of the compositions might become difficult
[0110] If the amount of water is too high, obtaining a workable consistency of the obtained paste when mixing the
compositions contained in the parts of the kit of parts described in the present text might become difficult, either. Further,
it will become difficult to achieve the desired mechanical properties.