Glass ionomer cement, process of production and use thereof european Patent Office ep 3079645 B1

Part A being a powder and comprising
-
an acid-reactive filler in an amount above 60 to 95 wt.%, the acid-reactive filler having a mean particle size in
the range of 3.5 to 10 mm,
-
a non acid-reactive filler in an amount above 5 to 30 wt.%, the non acid-reactive filler having a mean particle
size in the range of 1 to 3.5 mm,
-
Part A not comprising a polyacid in an amount of more than 1 wt.% wt.% with respect to the weight of Part A,
Part B being a liquid and comprising:
-
a polyacid in an amount above 35 to 60 wt.%,
-
water,
-
a complexing agent,
wt.% with respect to the weight of Part B
the weight ratio of Part A to Part B being from 2 : 1 to 4 : 1.
[0019] In another embodiment, the invention relates to a process for producing a hardenable composition comprising
the step of mixing Part A and Part B of the kit of parts as described in the text of the invention.
[0020] Moreover, described is a method of using the kit of parts and the cement composition obtainable or being
obtained by mixing the liquid and powder component as described in the text for dental purposes, in particular as dental
filling material, core build up materials or as root channel filling material.
[0021] Unless defined differently, for this description the following terms shall have the given meaning:
A "dental composition" or a "composition for dental use" or a "composition to be used in the dental field" is any composition
which can be used in the dental field. In this respect the composition should be not detrimental to the patients’ health
and thus free of hazardous and toxic components being able to migrate out of the composition. Dental compositions are
typically hardenable compositions, which can be hardened at ambient conditions, including a temperature range from

---