Glass ionomer cement, process of production and use thereof european Patent Office ep 3079645 B1

[0083] Suitable acid-reactive fillers are also commercially available from e.g. Schott AG (Germany) or Speciality Glass
(US).
-
The acid-reactive filler is typically present in the following amounts (wt.% with respect to the weight of Part A): from
above 60 to about 95 wt.%.
[0084] If the amount of the acid-reactive filler is too high, the compositions contained in the parts of the kit of parts
described in the present text cannot be adequately mixed, obtaining an adequate consistency and acceptable mechanical
properties might become difficult.
[0085] If the amount of the acid-reactive filler is too low, a suitable paste cannot be obtained by mixing the respective
compositions contained in the parts of the kit of parts described in the present text. Further, the mechanical properties
might become inferior.
[0086] The cement composition described in the present text contains non acid-reactive filler(s). A non acid-reactive
filler is a filler, which either does not cure in a glass ionomer reaction at all, if combined with a polyacid in the presence

---

EP 3 079 645 B1
8
5
10
15
20
25
30
35
40
45
50
55
of water, or only shows a delayed curing reaction.
[0087] A more precise definition of non acid-reactive filler is given above. The nature and structure of the non acid-
reactive filler is not particularly limited, either unless the desired result cannot be achieved. The non-acid reactive filler
is preferably an inorganic filler. The filler should be non-toxic and suitable for use in the mouth of a human being. The
filler can be radiopaque or radiolucent. The filler typically is substantially insoluble in water. "Insoluble in water" means
that less than about 1 or 0.5 or 0.1 wt.-% of filler dissolves in water, if 10 g filler is stirred in 100 ml water for 1 month.